ELECTROCHEMICAL DEPOSITION OF NICKEL COATINGS FROM ACETATE-CHLORIDE ELECTROLYTE IN PULSE MODE
Научная публикация
ELECTROCHEMICAL DEPOSITION OF NICKEL COATINGS  FROM ACETATE-CHLORIDE ELECTROLYTE IN PULSE MODE
Автор(ы): I. V. Antikhovich, S. M. Krupnik, A. A. Chernik, I. M. Zharski
УДК: The process of electrodepositing of nickel from acetate-chloride electrolyte at low temperature in a pulsed mode has been investigated. It is established that application of pulsed electrolysis mode allows to increase the working current density up to 9 A/dm2. A nanostructured nickel coating with a maxi- mum size of crystallites of 200 nm is obtained. The results show that the use of pulsed electrolysis makes possible to reduce porosity of coating thicknesses up to 20 μm
Год издания: 2012
Дата загрузки: 13.05.2014
Загрузил(а): Цылина И. А.

Описание:
The process of electrodepositing of nickel from acetate-chloride electrolyte at low temperature in a pulsed mode has been investigated. It is established that application of pulsed electrolysis mode allows to increase the working current density up to 9 A/dm2. A nanostructured nickel coating with a maxi- mum size of crystallites of 200 nm is obtained. The results show that the use of pulsed electrolysis makes possible to reduce porosity of coating thicknesses up to 20 μm

Использование электронных материалов, размещенных на данном сайте, осуществляется на договорной основе. Разрешается использовать ресурсы в единичном экземпляре и исключительно в личных целях.



Chemistry and Technology of Inorganic Materials and Substances