COMPOSITION OF PHOSPHATES FORMED BY THE INTERACTION OF LIQUID GLASS WITH ORTHOPHOSPHORIC ACID SOLUTIONS
Научная публикация
COMPOSITION OF PHOSPHATES FORMED BY THE INTERACTION  OF LIQUID GLASS WITH ORTHOPHOSPHORIC ACID SOLUTIONS
Автор(ы): A.I. Sumich, L.S. Eshchenko
УДК: 546.185:[544.77.022.822+544.77.022.823]
Год издания: 2013
Дата загрузки: 05.02.2015
Загрузил(а): Рогова О. А.

Описание:
The chemical and phase composition of products formed by interaction of liquid glass with 20– 80% H3PO4is investigated. It is shown that the products of the synthesis include hydrated silicon and phosphorus containing phases. The silicon containing phase is a mixture of amorphous silica gel and nonstoichiometric sodium silicates. The phosphorus containing phase is sodium hydrophosphate Na2HPO4· 12H2O. It is established that the crystalline phase is formed irrespective of a mixing method and acid concentration. It is suggested that the cause of formation of acid salt of phosphoric acid even at a large excess of water glass is replacement of protons H + of silanol ≡Si-OH-groups of silicic acid by cations of Na + and formation of sodium silicates which act as a connecting bridge between adjacent globules of the formed hydrogel.

Использование электронных материалов, размещенных на данном сайте, осуществляется на договорной основе. Разрешается использовать ресурсы в единичном экземпляре и исключительно в личных целях.



ChemistryTechnology of Inorganic Substances